Successful metal stitching requires precision, skill, and the right equipment. To ensure long-lasting repairs, we use:

Premium Pneumatic Tools

Imported pneumatic tools from leading U.S. manufacturers

Essential for preparing accurate profiles before stitching

Ideal for remote sites due to easy availability of compressed air

Key Features of the Metalock Process

Cold process — no heat, no distortion, no stress on castings

Precisely placed locks mechanically reinforce cracked sections

Restores structural integrity without welding

Ideal for engines and heavy machinery where alignment is critical

Engine lock after metal lock and metal stitching — Onsite Engine Block Repair

Advantages of Metal Stitching with Metal Keys

Keys are inserted across the crack to seal and tighten the casting

Overlapping patterns distribute load evenly

Repaired areas often become stronger than the original casting

Suitable for cast iron, aluminium, bronze, and cast steel

Cost-Effective Repair Solution

Metal stitching and metal locking provide a highly cost-efficient alternative to component replacement. Many industrial parts are:

Expensive to replace

Long lead-time items

No longer manufactured

Repairing them onsite saves money, reduces logistics, and keeps operations running smoothly.

Fast, Onsite, and Minimum Downtime

Metal stitching, a fast repair method, often enables completion within hours, directly at the site, without the need to dismantle the equipment. Metal stitching is a fast repair method that can typically be completed within hours, directly at the site, without dismantling the equipment. This drastically reduces downtime and allows machinery to return to service quickly.

Global Onsite Crack Repair Services

R A Power Solutions delivers onsite metal stitching, metalocking, engine block repair, and cast iron crack repair services in major industrial regions worldwide. Our teams are actively working on several international projects, providing reliable, high-precision solutions for critical equipment.

For inquiries or technical assistance:
📧 rajshahani@rapowersolutions.com

📧 info@rapowersolutions.com

📞 +91 9582647131, +91 9810012383.

With over 45 years of global experience, R A Power Solutions specialises in the onsite repair of cracked and damaged components using advanced metal stitching and Metalock techniques. We regularly undertake metal stitching and metalocking for heavy industrial parts made from cast iron, cast steel, aluminium, bronze, and other critical engineering materials. Components We Repair … Continue reading

When cast-iron or aluminum engine blocks crack, the traditional fix—welding—is often expensive, risky, and destructive. At RA Power Solutions, we specialize in advanced cold repair techniques—metal stitching and metal locking—that restore structural strength without applying heat, requiring machining, or dismantling equipment.

With the improvement in repair technology now, it is possible to repair the crack in cast iron, steel, or aluminium component by metal stitching and metal locking process. The main feature of repair of crack or damaged casting by metal stitching, metal locking, and metal surgery is that process does not require disassembly of the equipment and taking the crack or damaged part to the workshop.

What Are Metal Stitching & Locking?

Metal Stitching is a precise, cold repair method. Technicians drill a series of aligned holes across the crack, insert metal “keys” or studs into a dovetailed pattern, and tighten them so they interlock—effectively sealing the fracture and restoring rigidity.
Metal Locking reinforces the stitching with custom-shaped metal inserts that prevent the crack from spreading further and enhance the repair’s long-term durability

New Casting Inserted for Repair of Engine Block

RA Power Solutions has the team of experience technicians. They can travel to the site with tools and consumables required for metal stitching and metal locking undertake the repair.We repair cracks by metal locking and metal stitching while maintaining the original profile. In most cases, the process does not require any machining. Scientific tests prove that the repaired crack portion has greater tensile strength than before.

RA Power Solutions with the experience of forty five years in this field extends metal locking and metal stitching services for repair of damaged casting. We can also execute the repair while the vessel is sailing. We offer the lowest cost compared to our competitors.

Metal Stitching | Repair Cast Iron | Cast Iron Repair

Get your crack or broken components manufactured out of cast iron, cast steel or aluminium repair by metal stitching and metal locking process. RA Power Solutions with experience of more than four decades have successfully repaired thousands of major engine components and components installed in heavy industries all over the world.

The damage to the component may be serious, or the cracks are multiple. RA Power Solutions engineers have the experience, know how and necessary tooling to execute the most complicated and serious damage which takes place due to accidents in cast iron, cast steel and aluminium casting.

For more information on cold metal stitching engine block, cast iron engine block repair, metal stitching surgery, metal stitching engine block, repair cast iron, and metal stitching of engine block please email us at rajshahani@rapowersolutions.com or info@rapowersolutions.com, or call us at +91 9582647131 or +91 9810012383.

Metal Stitching & Metal Locking of Engine Block Under Process

Metal Stitching of Engine Block by Special Keys & Locks

FAQs:

1. What are metal stitching and metal locking?

Metal stitching involves drilling a series of aligned holes across a crack, inserting interlocking metal keys or studs, and tightening them to seal the fracture. Metal locking uses custom-shaped inserts that reinforce and prevent crack propagation.

2. Do these methods require dismantling the equipment?

No. We perform the repairs in situ, without disassembling the machinery or removing the damaged part from its position

3. Will the original surface or shape be affected by the repair?

We maintain the original profile after metal stitching and locking, and in most cases, no machining is needed afterward

4. Is the repaired area as strong as the original component?

Yes. Scientific studies show that crack areas repaired by metal stitching and locking often have greater tensile strength than before

5. Can repairs be performed while the vessel is underway?

Absolutely. We can execute repairs while the vessel is sailing, minimizing downtime and logistical challenges

When cast-iron or aluminum engine blocks crack, the traditional fix—welding—is often expensive, risky, and destructive. At RA Power Solutions, we specialize in advanced cold repair techniques—metal stitching and metal locking—that restore structural strength without applying heat, requiring machining, or dismantling equipment. With the improvement in repair technology now, it is possible to repair the crack … Continue reading “Metal Stitching | Metal Locking | Repair of Cast Iron by Metal Stitching – RA Power Solutions”

Category: Cast iron engine block repair

Metalock | Metal Stitching | Repair of Cracked Components

Components We Repair Using Metal Stitching & Metalock